POLYSTYRENE | MELAMINE CRYSTAL
Product Data Sheet
POLYSTYRENE | ABS | SD0150
Product Category
POLYMERS
| PROPERTY | TEST METHOD | TEST CONDITION | UNIT | VALUE |
|---|---|---|---|---|
| MFI | ASTM D 1238 | (200ºc/5kg) | Gr/10 min | 1.7 |
| 2 Izod Impact Strength (notched) | ISO 180 | 1/8 inch | Kj / m2 | 25 |
| Tensile Strength @ Yield | ASTM D | 5mm/min | Kgf /cm2 | 440 |
| Elongation @ Break | ASTM D | 5mm/min | % | 40 |
| Flexural Strength @ Yield | ASTM D | 2.8mm/min | Kgf /cm2 | 640 |
| Flexural Modulus | ASTM D | 2.8mm/min | Kgf /cm2 | 20500 |
| Vicat Softening Temperature | ASTM D | 5kg | ºC | 99 |
| Rockwell Hardness | ASTM D | - | R-Scale | 104 |
| Flammability | UL 94 | 1.5mm Specimen | Recognized | HB |
Application
auto parts, home appliances, electrical parts
Product Data Sheet
Product Category
POLYMERS
| PROPERTY | UNIT | VALUE |
|---|---|---|
| Purity | %(w/w) | >99.8 |
| Humidity | %(w/w) | <0.1 |
| PH | 7.5 | |
| Color | Hazen(Pt-co) | <20 |
| Turbidity | NTU | <20 |
| Size(below 80 mesh) | Mesh | 0.8 |
| Solubility in H2O | 20ºC clear | |
| Ash content | %(w/w) | <0.03 |
Application
Laminates, Adhesives, Molding compounds, Coating, Dishes
Product Data Sheet
POLYSTYRENE | GPPS | 1460
Product Category
POLYMERS
| PROPERTY | UNIT | VALUE | TEST METHOD |
|---|---|---|---|
| MFI (200oc/5kg ) | g/10 min | 6.5 | ISO 1133 H |
| Styrene residual monomer | PPM | <500 | CLGLABPSG004 (ATOFINA TEST METHOD) |
| Vicat softening point | OC | 103 | ISO 306A50 |
| Rockwell hardness | - | Scale L70 | ASTM D 785 |
| Tensile strength @ break | MPa | 48 | ISO 527-2 |
| Elongation @ break | % | 1 | ISO 527-2 |
| Tensile modulus | MPa | 3200 | ISO 527-2 |
| Refractive index | - | 1.591 | ISO Method |
| Water Absorption | % | <0.1 | ISO 62 |
Application
Insulation board (xps), foam sheet of food & fruits trays
Product Data Sheet
POLYSTYRENE | GPPS | 1540
Product Category
POLYMERS
| PROPERTY | UNIT | VALUE | TEST METHOD |
|---|---|---|---|
| MFI (200oc/5kg ) | g/10 min | 2.5 | ASTM D 1238 |
| Styrene residual monomer | PPM | <500 | CLGLABPSG004 (ATOFINA TEST METHOD) |
| Vicat softening point | OC | Min101 | ASTM D 1525 |
| Rockwell hardness | - | Scale L70 | ASTM D 785 |
| Tensile strength @ yeild | MPa | - | ASTM D 638 |
| Tensile strength @ break | MPa | 48 | ASTM D 638 |
| Elongation @ break | {5e002615228069c8628e44b1442e463d83f1aac768ac505617d5e5a7229c9fe6} | 3 | ASTM D 638 |
| Flexural modulus | MPa | 2900 | ASTM D 790 |
| Tensile modulus | - | 3200 | ASTM D 638 |
| Refractive index | - | 1.591 | ISO Method |
| Water Absorption | {5e002615228069c8628e44b1442e463d83f1aac768ac505617d5e5a7229c9fe6} | <0.1 | ASTM D 570 |
Application
Extrusion: Shower cabinets; Lighting thin films; Diluted with high impact polystyrene for thermoforming, it shows resistance against high temperatures. In line extrusion /thermoforming of transparent cups. •Direct gassing: Insulation board; Foamed sheet for thermoforming of fruit trays, meat trays, egg boxes.
Product Data Sheet
POLYSTYRENE | HIPS | 7240
Product Category
POLYMERS
| PROPERTY | TEST METHOD | UNIT | VALUE |
|---|---|---|---|
| MFI (200 o c/5kg ) | ASTM D 1238 | g/10 min | 4.5 |
| Styrene residual monomer | CLGLABPSG004 (ATOFINA TEST METHOD) | ppm | <500 |
| Vicat softening point | ASTM D 1525 | O C | Min.94 |
| Rockwell hardness | ASTM D 785 | - | Scale |
| Tensile strength @ yeild | ASTM D 638 | MPa | 21 |
| Tensile strength @ break | ASTM D 638 | MPa | 20 |
| Elongation @ break | ASTM D 638 | {5e002615228069c8628e44b1442e463d83f1aac768ac505617d5e5a7229c9fe6} | 55 |
| Flexural modulus | ASTM D 790 | MPa | 1750 |
| Tensile modulus | ASTM D 638 | MPa | 1800 |
| Izod impact | ISO 180/1A | {5e002615228069c8628e44b1442e463d83f1aac768ac505617d5e5a7229c9fe6} | Min. 8.5 |
| Water absorption | ASTM D 570 | {5e002615228069c8628e44b1442e463d83f1aac768ac505617d5e5a7229c9fe6} | <0.1 |
Application
Extrusion: Dirty sheet, Co extrusion with EVOH PE…, in dilution with crystal industrial sheet. Containers (up to 5 lit) Thermoforming: Cups, Trays, Egg boxes, General packaging. Dilution with crystal for CD inserts, Shoe heels.